DOBÓR PARAMETRÓW CIĘCIA / BIMETAL
DOBÓR PARAMETRÓW CIĘCIA DLA PIŁ BIMETALICZNYCH
Wymiar obrabianego detalu (mm) 50-125 mm
50–125 mm
Prędkość/wydajność cięcia
Typ materiału roboczego
prędkość piły m/min
Wydajność cm²/min
ABNT/AISI/SAE
Twardość
1005–1012
150HB
79–91
77–103
1015–1026
150HB
76–88
71–97
Stale węglowe
1030-1055, A36
175HB
55–67
52–58
1060–1095
200HB
49–61
39–52
1110-1117-1118
150HB
79–98
77–103
Łatwe w obróbce stale węglowe
1137–1151
175HB
67–79
52–77
1211–1215
150HB
79–98
97–120
1330–1345
200HB
55–67
39–52
1513–1527
150HB
79–91
77–103
Stale manganowe
1536–1552
175HB
61–79
52–65
1561–1572
200HB
49–61
39–52
4012–4024
175HB
61–73
45–58
Stale molibdenowe
4030–4042
175HB
58–70
45–52
4047–4068
175HB
55–67
39–52
4130–4140
200HB
55–67
39–52
Stale chromowo-molibdenowe
4142–4161
200HB
52–64
32–45
4320
175HB
61–73
45–58
4340
200HB
55–67
39–52
8115, 8615-8622, 8145, 8625-8637
175HB
61–73
45–58
Stale niklowo-chromowo-molibdenowe
8640-8660, 8740
200HB
55–67
39–52
8720, 8822
200HB
61–73
45–58
9310
175HB
49–58
19–26
9430–9445
200HB
55–67
39–52
Stale niklowo-molibdenowe
4615-4626, 4815-4820
175HB
61–73
45–58
5040–5060
200HB
55–67
39–52
5115–5120
175HB
61–73
45–58
Stale chromowe
5130–5160
200HB
55–67
39–52
50100, 51100, 52100
225HB
40–49
26–32
6118
175HB
61–73
45–58
Stale chromowo-wanadowe
6150
200HB
55–67
39–52
Stale krzemowe
9255–9262
200HB
55–67
39–52
A2-A6, A8-A10
200HB
55–67
19–26
Stale narzędziowe – do pracy na zimno
D2-D7, A7
250HB
20–30
13–19
O1, O2, O6, O7
200HB
55–67
26–39
H10-H19, H21-H42, P20
200HB
40–49
19–26
Stale narzędziowe – do pracy na gorąco
L2, L6
200HB
52–64
19–26
S1-S7
200HB
40–49
19–26
Stale narzędziowe węglowe
W1-W5
200HB
55–67
26–39
Ferrytyczne stale nierdzewne
405, 409, 430, 434, 436, 442, 446
175HB
24–30
19–26
42